Organic wool fiber and alkali solution method refinement

Author: WangHongYan
Tutor: PanFuKui
School: Qingdao University
Course: Textile Engineering
Keywords: wool fiber KOH n-butanol solution slenderizing quadratic general rotary unitized design optimum process
CLC: TS133
Type: Master's thesis
Year: 2009
Downloads: 64
Quote: 1
Read: Download Dissertation

Abstract


Slenderizing wool fiber by alkaline organic solution was studied in this paper.In order to solve the problem that alkaline agent can infiltrate into the inner part of wool fiber,KOH was used as alkaline agent and n-butanol was used as solvent instead of water. Thus,the expansion of fiber will decrease and the gaps among fibers will deflate. Consequently,the infiltration of alkaline agent will be slower than the reaction rate,and the inner part of wool fiber will not be damaged.Combining with the structure,chemical composition and properties of wool fiber, the action mechanism of slenderizing methods with alkali was introduced.The alkaline organic solution slenderizing process for wool fiber was investigated with quadratic regression rotation composite design and a mathematical model was set up of the fineness, breaking strength and breaking elongation related to the three major factors of the concentration of the KOH n-butanol solution,treatment time and the concentration of the penetrating agent.The optimum process parameters were obtained with the method of decision of multi-objective gray situation.The verification test also indicated the optimum process is right.The results show that the best slenderizing was achieved when the concentration of the KOH n-butanol solution was 7.2%,treatment time 7.7h,and the concentration of the penetrating agent 0.13%.Under the optimum process conditions,the scales are almost completely removed from wool fibers.The surface of the wool fibers is relatively smooth. And the main body of the wool fibers remains undamaged.The diameter decreases obviously;the breaking strength retention is high;and the elongation at break is slightly increased after the treatment.Now,research and application of slenderizing wool fibers by alkaline organic solution are still in primary and explorative stage.This topic can make the research and application of this method go further and more extendedly.

Related Dissertations

  1. The Study on High-Gauge Warp Knitting Suitability of Wool Underwear and Its Wear Performance,TS186
  2. Research on Slenderizing Jute Technical Fiber by Stretching,TS102.22
  3. Study on the Stretching Slenderization Modification of Yak Fibers,TS101.92
  4. Synthesis and Application of Solid Superacids SO42-/TiO2-HZSM-5 in the Preparation of Allantoin,TQ252.3
  5. Study on the Comprehensive Utilization of Apple Pomace,TS255
  6. Modification Mechanism of Wood Fiber Treated by Nano-SiO2 Sol and Processes of Wood/nano-SiO2 Composite,TB383.1
  7. The Ultrasonic Effect on Wool Fiber Properties and Its Low Temperature Dyeing,TS193
  8. Bulk Nd2Fe14B/α-Fe Nanocomposite Magnets Perpared by Hot Deformation,TM273
  9. Study on Optimization of the Large-Scale Coal-fired Station Circulating Water System Operating,TM621
  10. The Screening Virulent Strains of Metarhizium Anisopliae and Beauveria Bassiana to Locusta Migratoria Manilensis (Meyen) and the Study of Application,S476.1
  11. Preparation and Application of Nano-Neodymium Oxide and Magnesium Hydroxide Whisker,TB383.1
  12. The Research of Technique Used in Identification of Cashmere and Sheep Wool Fiber,TS102.3
  13. Study on Color Correction of Dunhuang Mural Reproduction,TP391.41
  14. The Structures and Thermal Properties of Cashmere Fiber,TS102
  15. Study on Qualities Analysis of Cashmere Raw Material Based on IR Spectroscopy and FESEM Technology,TS131.8
  16. Study on Purifing Indoor Air with Wool Fiber Modified by Nano-TiO2,TU834.8
  17. The Study of the Preparation Technology of Horniness Surface Layer on Piston Ring,TG174.4
  18. Analysis and Characterization of the Secondary Structure of Slenderized Wool Fibers,TS102.311
  19. Research on Cashmere Stretching Slenderization Processing and Mechanism,TS133
  20. Application and Study on FTIR Microspectroscopy of Textile Fibers,TS101.9

CLC: > Industrial Technology > Light industry,handicrafts > Textile industry,dyeing and finishing industry > Wool Textile > Raw wool early processing
© 2012 www.DissertationTopic.Net  Mobile