The Study on the Preparation and Modification of the Asphalt Resin Composites

Author: ZhangXiuChen
Tutor: ChaQingFang
School: China University of Petroleum
Course: Chemical processes
Keywords: Asphalt resin composites Hardness Heat resistance Modified Microwave
CLC: TB332
Type: Master's thesis
Year: 2009
Downloads: 155
Quote: 1
Read: Download Dissertation

Abstract


Asphalt resin exhibits processing convenience, easy molding, tensile strength and modulus almost equivalent to phenolic resin, very good compatibility with carbon materials and excellent sliding friction properties. The composites with asphalt resin and graphite behave low surface energy, small tribological coefficient and suitable for the conditions of dry friction. Nevertheless, the asphalt resin composites with graphite shows serious abrasion problem, due to its lower hardness and poor heat resistance at high temperature, in the practical application.The purpose of this paper was to improve the hardness and heat resistance of asphalt resin composites and its wear resistance ulteriorly. In the first place, in order to improve the hardness and heat resistance of asphalt resin composites, the process conditions of preparing asphalt resin composites were optimized. Secondly, the effects on the properties of asphalt resin composites caused by different raw materials and cross-linking agents were tested respectively. In the next place, in order to improve the hardness and heat resistance of asphalt resin composites, physical and chemical modifications were studied. Different fillers were added to the composites in the physical modification. In the synthesis of asphalt resin, inorganic acid L and phenol were added as reactants. The properties of asphalt resin composites were studied in the physical and chemical modification. At the last, the application of the microwave in the preparation and modification of asphalt resin composites were preliminarily investigated.The better conditions of the preparation of asphalt resin composites were as follows: the mixed ratio of asphalt resin and graphite was 3:7; the molding pressure was 30MPa, the particle size was 120 mesh or more; the dwell time was 5 minutes; the preheating temperature is 220℃. The asphalt resin composites exhibited the best heat resistance and hardness, when the trioxane as cross-linking agent synthesized asphalt resin. When the temperature was under 300℃, the properties of asphalt resin composites that was deoiled asphalt as the raw material exceeded that with coal tar pitch. When the temperature preponderated over 300℃, the result was reverse. Adding 10% lanthanum oxide or 8% inorganic acid L and 12% phenol could improve the performance of asphalt resin composites to some extent. Adding lanthanum oxide and inorganic acid L had more obvious effect on the asphalt resin composites. The treatment of the microwave could not only shorten the preparation time of asphalt resin composites but also could improve the performance of asphalt resin composites. Through the modifications and microwave treatment, the hardness of the asphalt resin composites prepared in this paper could increase 100% and the mass loss rate of the asphalt resin composites calcinated for ten hours at 350℃could reduce from 12% to 3% or less.

Related Dissertations

  1. Process Optimization and Degradation Kinetics for Microwave Vacuum Drying of Different Traditional Chinese Medicine Extract,TQ461
  2. Synthesis and Application of the chloro- methoxy fatty acid methyl esters,TQ414.8
  3. Under microaerobic conditions closed calcium carbide furnace exhaust COS gas adsorption purification,X781
  4. Situ synthesis of mullite stone whisker toughening microwave metallurgical corundum - mullite Refractories,TQ175.6
  5. Synthesis and Application of A Novel Series of Cation Hydrophobically Modified Polyacrylamide,TQ323.6
  6. Study on Technics & Performance of Nano Electroless Composite Plating on 20~# Steel,TQ153
  7. Curing Mechanism and Properties of Fluorenyl Epoxy Resin,TQ323.5
  8. Preparation, Characterization and Application of Prussian Blue Composite Nanomaterials,TB383.1
  9. Study on Quality Change and Prediction Model for Shelf-life of Chilled Pork,TS251.4
  10. Soil Erosion Simulation in Hilly Area of South China,S157
  11. Adsortions of Dye by Modified Activated Carbon and Heavy Metals by Rice Husk-Based Activated Carbon,X703
  12. Study on Organic Silicone Modified Epoxy Resins Performance and Preparation of Adhesive,TQ323.5
  13. Spectral and Electrochemical Research of Epirubicin Hydrochloride with Its Analytical Application,TQ465
  14. The Synthrsis of Novel Purine Nucleoside Modified by C~6-Alkyl and C~6-Heterocyclic,TQ460.1
  15. Silicone modified acrylic emulsion research,TQ633
  16. Synthesis and Characterization of Modified PA-6 Containing Aromatic Ring,TQ323.6
  17. Research on Fabrication of Sc2O3 Nanopowders and Transparent Ceramics,TQ174.1
  18. ATO zeolite microwave synthesis and hydroisomerization of n-decane Performance,TQ424.25
  19. Study on Blending Modification of Biodegrable Plastics PBS,TQ323.4
  20. Study on Composite Modification of CaO-based Sorbent,TQ424
  21. Research on Synthesis and Application of Novel Benzoxazine,TQ323.1

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Composite materials > Non-metallic composite materials
© 2012 www.DissertationTopic.Net  Mobile