Dissertation > Excellent graduate degree dissertation topics show

Fabrication of HA Porous Scaffold by Freeze-Drying

Author: WangXinJuan
Tutor: ZhaoKang
School: Xi'an University of Technology
Course: Materials Science and Engineering
Keywords: hydroxyapatite freeze-drying lamellar porous compressive strength in vitro test
CLC: R318.08
Type: Master's thesis
Year: 2008
Downloads: 178
Quote: 1
Read: Download Dissertation

Abstract


A new porous ceramic preparing method, freeze-drying has been developed in recent years. It provides lamellar pores by removing the liquid from frozen body. The character of lamellar pores can be controlled by freeze-drying parameter and sintering temperature. In this paper, the porous hydroxyapatite (HA) scaffolds with lamellar pores structure were fabricated by freeze-drying. The properties including pores morphology, size, and distribution were investigated; the mechanical properties were tested by Instron5565 material testing. The results show that the scaffolds have an open, unidirectional and interconnected lamellar structure with a porosity between 45～85%, and with pore size between 50～400μm, The volume fraction of HA powder played an important role preparing of the scaffolds. The volume fraction of HA powder between 30～35% could fabricate lamellar scaffold, while slurry with HA powder 30%vol could obtain scaffold with porosity between 60～65%. The pore size of HA scaffold were controlled by freeze temperature, when the temperature were -10℃、-30℃and -196℃respectively, the pore size were 350～400μm、200～250μm、50～100μm.The results of compressive have a great relationship with porosity and pore size distribution; the compressive strength decrease gradually with the increasing of porosity and pore size. When sintered temperature and time was 1250℃, 2～6h, the compressive strength of 7.9MPa was obtained at porosity 65%, and pore size 200～250μm.The porous scaffold was proved to have a good compatible by vitro cellular assay. The osteoblast-like cells were attached and spread well throughout the porous scaffold, while the pore size and the porosity were 200～250μm and 65%, the absorbance of HA scaffold was 0.26 Arbit.unit.

Related Dissertations

  1. Experimental Study of Porous Composite Materials on the Base of Recycled Concrete Powder-Cement,TU528
  2. The Experimental Research on Regeneration Aggregate and Proportioning of Recycled Concrete Brick,TU528
  3. Recycled aggregate semi- rigid concrete preparation and molding of test,TU528
  4. Effects of Low Molecular Organic Acids on Immobilazition of Lead Ions by Nanosized Hydroxyapatite,S153
  5. Acid solution on the structure and properties of chitosan / hydroxyapatite composite,R318.08
  6. Establishment of Protocol for Preparation and Assay of Lysin Encoded by Bacteriophage from Streptococcus Suis,R515
  7. Cultured Bacillus Japanese beetles and freeze-drying protectants recovery of,S482.3
  8. Preparation of tricalcium silicate and silicon physicochemical properties of calcium phosphate cement,R318.08
  9. Fibroin microspheres and their use as cell carriers in study,R318.08
  10. Needle Coke Powder Molding Process and Its Impact on the Performance of Carbonization Products,TQ127.11
  11. Preparation of Unfired Bricks by Industry Sludge Solidified Cement and Analysis of Economy and Technique,X703
  12. Study on FRP Confined Rectangular Concrete Columns,TU375.3
  13. Preparation, Characterization and Performance of the Bio-coatings on the Surface of Pure Titanium Based on Micro Arc Oxidation,R318.08
  14. Hard casting gas and environmentally friendly water-soluble polymer binder hardening mechanism of,TG221.1
  15. TC4 alloy pulsed laser deposition of hydroxyapatite microstructure and properties of,TG146.23
  16. TiO 2 nano flowers and HAP / TiO 2 Preparation, Characterization and Photocatalytic Degradation of Organic Pollutants,O643.32
  17. Lightweight foam soil mixed flow regime Prevention Research Bump,U414
  18. Stirrups confined concrete performance Size Effect,TU375
  19. Study on Repairing Material of Cement Concrete Pavement Which Based on Slag,U414
  20. Study on Implant Material of Carbon/Carbon+Hydroxyapatite Coating (C/C+HA) Composites,R318.08
  21. The Study on the Biodegradable Polylactic Acid Composites,R318.08

CLC: > Medicine, health > Basic Medical > Medical science in general > Biomedical Engineering > General issues > Biomaterial
© 2012 www.DissertationTopic.Net  Mobile