Ceramic Theramal Sterss Cleaving Technology Based on Laser

Author: TianZhongGuo
Tutor: WangYang
School: Harbin Institute of Technology
Course: Aviation Aerospace Manufacturing Engineering
Keywords: Continuous Nd: YAG Laser Laser Cutting Thermal Stress Cleaving Alumina Zirconia
CLC: TQ174.62
Type: Master's thesis
Year: 2011
Downloads: 12
Quote: 0
Read: Download Dissertation

Abstract


Ceramic is widely used in the aerospace, MEMS, and daily life. The traditional methods of slicing ceramics are based the diamond saw. These methods are difficult and expensive to process ceramics due to hardness and brittleness et al, The research about controlled fracture method based on laser cutting technology is widely focused in recent years. The thermal crack technology has many advantages, Such as high efficiency, high cutting quality and cleaning machining environment. Ceramic thermal crack cutting technology based on continuous YAG laser has small heat affected zone, smooth crack surface and no loss of materials, and so on.This dissertation carried out the thermal analysis and cutting experiment, according related researcher’s researching progress, and the rationale between laser and ceramic.Firstly, symmetrical cutting of ceramic was simulated by using Finite Element Methods. Mechanism of YAG laser cutting glasses was studied, according to the simulation temperature and stress fields. Comparison between simulation temperature and testing temperature is carried. Give analysis to the cleaving deviation at the start crack path.White ZrO2 ceramic has low absorption rate to the continuous YAG laser. Graphite coated ceramic surface can effectively improve the absorption rate to laser. Experimental research on white and black Zirconia ceramic, Alumina ceramic and a kind of machinable ceramic were cutting. A series of single factor experiment have carried to black zirconia ceramic. Nano-indentor, Surface Profiler and SEM are used to test the result.Finally, the optimum parameters of YAG laser cutting black zirconia ceramic in straight lines were obtained. The width of color change area and Roughness of crack surface are tested, and gives the curve to laser power, laser spot size and laser scanning velocity, respectively.

Related Dissertations

  1. Gel - Foam Preparation of porous alumina insulation materials,TQ174.1
  2. 12-Tungstophosphoric Acid Modified-Zirconia Aerogel as a Solid Acid for THF Polymerization,TQ316.314
  3. Different metal base and binder zirconia all-ceramic crowns on the color of,R783
  4. Lithium anode material calcined alumina crucible Development,TQ174.6
  5. Within the connection developed to detect its mechanical properties of zirconia abutment,R783.6
  6. CFD Simulation and Verification Experiment of Fluidized Bed with a Adjustable Slit Height Blast Cap,TQ051
  7. Synthesis, Characterization of Co3O4 /Al2O3 Nanomaterials and Catalytic Degradation on Rhodamine B,TB383.1
  8. Based on the porous structure to improve efficiency of LED light,TN312.8
  9. Modified LaMnO 3 perovskites for catalytic combustion of low concentration methane,O643.36
  10. Precipitation from aqueous solution ultrafine spherical alumina Process,TB383.3
  11. Porcelain steel surface preparation in the lining layer of Technology,TG174.45
  12. Porcelain surface lining layer performance and organizational analysis,TG174.44
  13. One -dimensional properties of the material humidity,TB383.1
  14. Nano zirconia thermal barrier coatings prepared by plasma spraying and Properties,TG174.442
  15. Alumina vacuum carbothermal reduction experimental study of the mechanism and process - aluminum chloride process,TF821
  16. Alumina vacuum carbothermal reduction experimental study,TF821
  17. Processing and Characterization of Short Fiber-reinforced Aluminium Matrix Composites,TB333
  18. Preparation and Characterization of Building Waterborne Thermal Insulation Coating Using Composite Technology,TQ630.7
  19. Microstructure and Properties of Highly Porous Al2O3 Ceramics by Freeze-casting,TQ174.1
  20. Synthesis and Application of Mesoporous Alumina,O614.31

CLC: > Industrial Technology > Chemical Industry > Silicate > Ceramic Industry > Production process and equipment > Blank,forming
© 2012 www.DissertationTopic.Net  Mobile