Preparation & Application of Magnetic Nano-Particles

Author: JiangLin
Tutor: GaoFeng
School: Shanghai Jiaotong University
Course: Chemical Engineering and Technology
Keywords: Fe3O4 Fe3O4/SiO2 composed particles Fe3O4/Au Immunochromatographic
CLC: TB383.1
Type: Master's thesis
Year: 2009
Downloads: 417
Quote: 1
Read: Download Dissertation

Abstract


As a new functional material, magnetic particles have been developed quickly in recent years. It’s applications in immunoassay lead to a new idea for bioseparation and detection. The development of magnetic particles with functional unites was described in this paper.Fe3O4 nanoparticles were synthesized from an aqueous Fe （OH）2 suspension by oxidizing it with H2O2, the size of which can be controlled by adjusting the temperature, the concentration of the oxidation and pH of the solution. The reaction took place under the neutrality condition, and can produce particles with good magnetic properties and dispersity, which is profitable for the application of the magnetic particles on biomedical use. We produced Fe3O4/Au core-shell composite particles by means of reducing HAuCl4 with NaBH4 with good dispersity in water after magetic separation. The UV spectra showed the maximum absorption at the peak of 549nm, the character peak of nanogold, and the average diameter of the nano particle was about 30nm according to TEM image. The characteristic peak of Au was found in the XRD spectra of nano-composites, which demonstrated Fe3O4 nanoparticles were coated with layers of Au. The Fe3O4@Au nano-composites were equipped with the properties of gold nanoparticles and magnetic nanoparticles, which broadened the applications in the bio-medical field.We provided a new method of synthesizing Fe3O4/SiO2 nanoparticles. The Fe3O4 nanoparticles first modified by KH560 to enhance the monodispersity in C2H5OH, and then treated with TEOS to prepare the Fe3O4/SiO2 composites which were well dispersed and with uniform size around 25nm, of which the thickness of the shell is about 3nm. According to the TEM image, we successfully got the shell/core nano-particle structure and the saturation intensity is about 44.03emu/g. Because of the good dispersity in the water, the nano magnetic composites can be better used in bio-medical field.Last but not the least, an immunochromatographic strip for the simple and rapid detection ofα-fetoprotein（AFP） is developed with the technique of the anti-AFP monoclonal antibodies labeled with nano-magnetic particles. The factors influencing the label-process as well as the sensitivity and the key process of the strip making are studied. The prepared strips can show the detection of the cut-off value for positive result was 20μg/L AFP within ten minutes. Compared with the gold immunochromatography, the new technique can reduce the cost notably and optimize the whole process.

Related Dissertations

  1. Synthesis of Magnetic Fe3O4 Microparticles and SiO2/Fe3O4 Composite Spheres,TB383.1
  2. Preparation and Characterization of Multifunctional Fe3O4/ZnO/SiIO2 Nanocomposites,TB383.1
  3. Development of Monoclonal Antibody to Rabbit Hemorrhagic Disease Virus and Establishment of Detection Methods to the Virus,S858.291
  4. Investigation on Preparation and Properties of Core-Shell Structural Magnetic Nanocomposites Based on Layered Double Hydroxides,TB383.1
  5. Preparation of Hollow Fe3O4 Drug-loaded Magnetic Nanoparticles and Drug Releasing Properties Investigation in Vitro,R944
  6. Preparation of Magnetic Separable TiO2 Nanocatalysts and the Study of Its Photocatalytic Ability,O643.36
  7. Studies on Oxygen Reduction Reaction of Pt/C Electro-catalyst Modified by Fe3O4,TM911.4
  8. Synthsis and Property Study of Fe-Based Oxides and Fe-Based Oxides/GNS Nanocomposites,TB33
  9. Preparation of Magnetic Fe3O4 Nanoparticles and the Study of Their Relaxation Properties,TB383.1
  10. Study on Folic Acid Click Chemistry Functionalized Gold Materials and Its Sensing Properties,TB383.1
  11. Preparation of iron pyrite wastewater Black Pigments,TQ621.2
  12. Study on Colloidal Gold Immunochromatography Technique for Rapid Detection of Chloramphenicol Residues in Food,R155.5
  13. Preparation and Characterization of Magnetic Composite Microspheres and Their Application in Purification of DNA,TB383.4
  14. Preparation and Characterization of Fe3O4 Nanoparticles Coated with Organic Compounds,TB383.1
  15. Degradation of Atrazine and 2, 4-D by Nanoscale Fe3O4 and Microorganism Integrated Treatment System,X172
  16. Preparation of Nano-fe 3 O 4 Particles Induced by Weak Exterior Magnetic Fieldand Magnetic Fluid Stability Study,TB383.1
  17. Formation and Magnetic Characteristion of Magnesium Oxide / Iron Nano Composite Materials,TB383.1
  18. Preparation of Amino Group and SiO2 Coated Fe3O4/Polystyren Magnetic Spheres,TB383.4
  19. Structure and Microwave Absorption Properties of Poly（Ppyrrole） Coated Fe3O4/Multiwalled Carbon Nanotube Composites,TB383.1
  20. Fe_3O_4 magnetic particles and polystyrene microspheres Preparation and Characterization of LB films,TB383.1
  21. Ultrasonic Enhanced Degradation of Rhodamine B by Fe3o4/h2o2 and Ultrasonic Extraction of Cyanuric Acid in Pet Food,TS207.5

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Special structural materials
© 2012 www.DissertationTopic.Net  Mobile